Silicone Coating film-forming temperature is low, and the film can be formed fully at 220℃. The film can be directly hand touch after surface drying for 5 minutes. The thermal resistance and open fire resistance are better than those of the conventional organic silicon, and coating without cracking. The production efficiency is improved and energy conservation, low emission, and lower defect rate.
Silicone Coating can be widely used in the external spraying of cookware. High chemical resistance series is widely used in food baking pans, cookware, etc.
1.Low-temperature curing: After curing for 10 minutes at 220℃, it can reach the performance of ordinary 280℃ organic silicon products.
2.Energy conservation: The low-temperature baking can reduce the energy consumption during production so as to reduce the cost.
3.Efficiency: The efficiency can be improved through raising the baking temperature. 280℃×4min, 290℃×3min and 300℃×2min for drying. Compared with the production efficiency of the traditional organic silicon, it is improved by more than one time.
| Curing temperature | 220-300℃ |
| Film thickness | 15-30μm |
| Material pre- treatment | Sand blasting/ Degreasing |
1.Silicone Coating can be widely used in the external spraying of cookware.
2.High chemical resistance series is widely used in food baking pans, cookware, etc.